Battery PE separator for lithium Ion Battery

High Purity Innovative Materials

Battery PE separator for lithium Ion Battery

Quality Control: Each lot of NANOSHEL Battery PE separator was tested successfully.

PE Separator - SEM

PE Separator – SEM

PE Separator

Battery PE Separator

Product Name Battery PE Separator
Stock No. NS6130-10-1185
Appearance Ivory-white
Thickness Micron 16±2
Gas permeability Sec/100ml 350-550
Porosity % 38-44
Puncturing Strength g >300
Tensile strength MD Mpa >90
Tensile strength TD Mpa >100
Film close temperature ≤135
Film break temperature ≥147
90℃ heat shrink MD % ≤3.5
90℃ heat shrink TD % ≤2
105℃ heat shrink MD % ≤5
105℃ heat shrink TD % ≤3
120℃ heat shrink MD % ≤20
120℃ heat shrink TD % ≤15

Experts Review:

58496396

Dr. Bruce Perrault, Ph.D (Georgia Institute of Technology (Georgia Tech), USA)
Lithium–ion batteries seem to be everywhere these days. They power most of the electronic devices we carry around with us such as- Consumer Gadgets, Electric Cars, Cell phones, Digital cameras, MP3 Players, Laptops and so on. Due to their good energy-to-weight ratio, lithium batteries are some of the most energetic rechargeable batteries available today. They get their name from lithium ion that moves from the anode to the cathode during discharge and from cathode to anode during recharging.


1252525

Dr. Myron Rubenstein, Ph.D (Polytechnic University of Turin, Italy)
Space and military sectors use Lithium-ion batteries as portable power sources and in future, spacecraft like James Webb Space Telescope are expected to use lithium-ion batteries. The main reason for this rapid domination of lithium-ion battery technology in various sector is the highest storage capacity with respect to its weight.


2536582

Dr. Huojin Chan (University of Science and Technology of China, Hefei, Anhui, China)
Lithium-ion batteries are suitable for applications where both high energy density and power density are required, and they are superior to other types of rechargeable batteries such as lead-acid, nickel-cadmium, nickel-metal hydride etc. due to following aspects: (1) store more energy and deliver higher power for longer duration of time (2) get charged in shorter period of time (3) have a longer life time (4) be resistant to fire hazards.


10604509_1459864657612760_2405225879143508610_o

Dr. Ms. Yi Yen Shi, (King Mongkut’s University of Technology Thonburi,Bangkok, Thailand)
Now a days there is a great deal of interest to upgrade the exisiting LIBs with improved properties & a battery technology that would permit smart storage of electric energy. With the avident of next generation LIBs, electric vehicles are expected to cover longer distances with shorter charging time, mobile phones and laptops are expected to be charged within minutes and last longer.


125448

Dr. Hans Roelofs Ph.D (National Technical University of Athens, Greece)
Nanotechnology has the potential to deliver the next generation batteries, especially lithium-ion batteries, with improved performance, durability and safety at an acceptable cost. A typical lithium-ion battery consists of three main components: an anode made of (mainly graphene and other conductive additives), a cathode (generally a layered transition metal oxide) and electrolyte through which lithium ions shuttles between the cathode and anode during charging and discharging cycles.


Battery PE separator

Battery PE separator

Contact Us for Battery PE separator
free quote

From us, you can easily purchase nano materials at great prices. Place online order and we will dispatch your order through DHL, FedEx, UPS. You can also request for a quote by mailing us at sales@nanoshel.com Contact: +1 302 268 6163 (US and Europe), Contact: +91-9779550077 (India). We invite you to contact us for further information about our company and our capabilities. At Nanoshel, we could be glad to be of service to you. We look forward to your suggestions and feedback.

More Lithium Ion Battery Materials By Nanoshel

NS6130-02-269 – LITHIUM IRON PHOSPHATE Nanopowder (LiFePO4, Purity: >99.5%, 80-100nm)

NS6130-02-279 – Lithium Manganese Oxide (LiMn2O4, Purity: >99%)

NS6130-02-286 – LITHIUM COBALT OXIDE Nanoparticles (LiCoO2, APS<100nm, Purity: 99.9%)

NS6130-10-1185 – PE separator for lithium Ion Battery

NS6130-12-000064 – Copper Foil (Cu, Purity: >99.8%, APS: <20μm)

NS6130-12-000318 – Lithium Titanate Oxide Powder (Li4Ti5O12,Purity: >99%, APS: 2μm )

NS6130-12-000319 – Lithium Nickel Manganese Cobalt Oxide (LiNiMnCoO2, Purity: 99.9%, APS: ≤ 25.0µm)

NS6130-12-000321 – Meso Carbon Micro Beads (MCMB, Purity: 99.8%, APS: 15.0-20.0µm)

NS6130-12-000328 – Copper Foil (Cu, Purity: >99.8%, Thickness: 10μm)

NS6130-12-000329 – Copper Foil (Cu, Purity: >99.8%, APS: <12μm)