High Purity Ferromagnetic Carbon Nanotubes
Product: Ferromagnetic Carbon Nanotubes
Description: Sample purity of NANOSHEL Ferromagnetic Carbon Nanotubes (MWNT 99% Dia:20-30nm Length:30-40um) is 80-98 Vol%, as determined by Raman Spectrophotometer and SEM Analysis. Nanoshel Nano material contains no residual catalyst impurities. Tubes occur in bundles of length ~1 – 20μm (±1.5μm). Individual tube length has not been determined.
|Materials||Ferromagnetic Carbon Nanotubes|
|Residue ( calcination in air)||<1%||Confirm|
|Average interlayer distance||0.34nm||Confirm|
|Special surface area||90-350* m²/g||Confirm|
|Bulk density||0.05-0.17 g/cm³||Confirm|
|Real density||1-2 g/cm³||Confirm|
|Charging *||2180 (Capacity: mA h/g)||Confirm|
|Discharging*||534 (Capacity: mA h/g)||Confirm|
|Volume Resistivity||0.1-0.15 Ω.cm ( measured at pressure in powder)||Confirm|
|Available Quantities||10Gms, 25Gms, 50Gms, 100Gms and larger quantites|
|Main Inspect Verifier||Manager QC|
Dr. Ms. Kelley Johnson, Ph.D (Adam Mickiewicz University in Poznań, Poland)
Multi walled carbon nanotubes consists of multiple rolled layers (concentric tubes) of graphite. Their diameter is 3-30 nm and they can grow various cm long, thus their aspect ratio can vary between 10 and ten million. MWCNT have Russian –doll Structure, rigidity, smaller outer diameter, different wall structure, and hollow interior.
Dr. Richard Harper, Ph.D (National Polytechnic Institute (IPN), Mexico)
MWNTs are highly conductive when properly integrated into a composite structure. The outer wall alone is conducting, the inner walls are not significant to conductivity. MWNTs have a high aspect ratio with lengths typically more than 100 times the diameter, and much higher. Their performance and application is based not just on aspect ratio, but also on the degree of entanglement and the straightness of the tubes, which in turn is a function of the both the degree and dimension of defects in the tubes.
Dr. Juan Yang (Seoul National University Seoul, South Korea)
MWNTs with no defects have an excellent tensile strength and when integrated into a composite, such as a thermoplastic or thermoset compounds, can significantly increase its strength. MWNTs have a thermal stability more than 600 °C, based on the level of defects and to certain extent on the purity as residual catalyst in the product can also catalyze decomposition.
Dr. Steve Chesney, Ph.D (Ludwig Maximilian University of Munich,Germany)
MWNTs are an allotrope of sp2 hybridized carbon similar to graphite and fullerenes and as such have high chemical stability. To enhance the both Strength and dispersibility of composites one can functionalize the nanotubes.
Dr. Ms. Mia Liao (National Taipei University of Technology, Taiwan)
MWNTs are suitable for various applications due to its high conductivity and high aspect ratio. The needed conductivity level can be achieved with much lesser loadings than for conventional solutions such as metal particulates or carbon black. Applications are: electrostatic discharge protection in wafer processing fabrication, antistatic elastomeric and plastic components for automobile fuel line components, plastics rendered conductive to enable electrostatic spray painting of automobile body parts, RFI shielding materials, etc.
From us, you can easily purchase nano materials at great prices. Place online order and we will dispatch your order through DHL, FedEx, UPS. You can also request for a quote by mailing us at firstname.lastname@example.org Contact: +1 302 268 6163 (US and Europe), Contact: +91-9779550077 (India). We invite you to contact us for further information about our company and our capabilities. At Nanoshel, we could be glad to be of service to you. We look forward to your suggestions and feedback.
More MWCNT By Nanoshel
NS6130-06-647 – Multi Wall Carbon Nanotubes (OD: 20-30nm, Length: 15-30µm, Purity:95%)
NS6130-06-648 – Multi-Wall Carbon Nanotubes/natural rubber nano composite
NS6130-06-685 – Carbon Nanotubes Silver Nanoparticles (MWNT 99%, Dia:20-30nm Length:30-40µm)
NS6130-06-686 – Twisted Aligned Carbon Nanotube/Silicon Composite Fiber (99%)
NS6130-06-687 – Carbon Nanotubes/Cobalt Sulfide Composites as potential high-rate (99% OD:20nm L:40µm)
NS6130-06-688 – Carbon Nanotube Magnesium Composites (MWCNT 99% Dia:20-30nm Length:30-40µm)
NS6130-06-689 – Carbon Nanotube Silver Composite for Mercury Capture and Analysis (99%, Dia:20nm Length:40µm)
NS6130-06-690 – Silicon Coated Carbon Nanotubes (99% Dia:20-30nm Length:30-40µm)
NS6130-06-691 – Ferromagnetic Carbon Nanotubes (MWNT 99% Dia:20-30nm Length:30-40µm)
NS6130-06-694 – The Nickel Oxide/CNT Composites with high Capacitance for Supercapacitor
NS6130-06-695 – Iron Filled Carbon Nanotubes (MWNT 99% Dia:20-30nm Length:30-40µm)
NS6130-06-696 – Pure Carbon Nanoscale Devices Nanotube Heterojunctions (MWCNT, 99.99%)