EVA Foam Sheet (Ethylene Vinyl Acetate blended copolymers)

EVA Foam Sheet

Product: EVA Foam Sheet (Ethylene Vinyl Acetate and blended copolymers)

Quality Control: Each lot of NANOSHEL EVA Foam Sheet was tested successfully.

EVA Foam Sheets Image

EVA Foam Sheets

Product Name EVA Foam Sheet
Purity >99.9% Confirm
Density 30 kg/m3 Confirm
Surface Hardness 40 °C Confirm
Tear Strength 0.35 N/mm m² Confirm
Tensile Strength 780 Kpa Confirm
Elongation at break 100 % Confirm
Compression Strength 78 Kpa Confirm
Compression deformation 25 % Confirm
Size Change Rate 0.8 % Confirm
Rebound Rate 26.00 % Confirm
Elongation 130 % Confirm
Service Temperature -30 to 180 °F Confirm
Thermal Conductivity 0.038 W/mK Confirm
Adhesive Thickness 0.15 mm Confirm
Adhesive Weight 80 g/m³ Confirm
Adhension 18 N/25 mm Confirm
Application +10 °C min Confirm
Service -50~+100 °C Confirm
Short peak +120 °C Confirm
Storage 3 year Confirm
Conclusion The specifications Confirm with enterprise standard
Main Inspect Verifier Manager QC

Experts Review:

Terence Mitchell, PhD,(ICAI School of Engineering Madrid, Spain)Terence Mitchell, PhD,(ICAI School of Engineering Madrid, Spain)
Foams are materials with a large amount of interfaces- free surfaces- with the potential to show radiation resistance due to ideally unsaturable sink strength represented by free surfaces. Nanocomposites, Nanophase materials, and Nanofoams could be unusually resistant to radiation because radiation-induced point defects cannot accumulate in the presence of the high density of defects sinks provided by interfaces and surfaces in these materials.


Dr. Ms. Huian Ruan(Taungoo Technological University, Myanmar)Dr. Ms. Huian Ruan(Taungoo Technological University, Myanmar)
Foams are dipped into molten metal, then placed in a vacuum so that the air in the foam’s pores is removed and replaced by the alloy. The foam had pore sizes of about 2mm, that can be tuned to create a stiffer or more flexible materials. During testing of its strength material showed an ability to deform when heated above 144 degrees, regain rigidity when cooled, then return to its original shape and strength when reheated.


Dr. Guowei Kwong, PhD(Ho Chi Minh City University of Science, Vietnam)Dr. Guowei Kwong, PhD(Ho Chi Minh City University of Science, Vietnam)
Amorphous metal foams are highly ductile in compression, and thus offer attractive compromises in mechanical and physical properties between crystalline metallic and ceramic foams. Metal foams have properties which make them suitable for automotive industry,  in ship building, aerospace industry and civil engineering.


EVA Foam Sheet

EVA Foam Sheet



Nanoshel’s Product Categories Link:

ZnSe/ZnS QDs WATER SOLUBLE, InP ZnS QDs SURFACE MODIFIED, CdS/ZnS QDs H2O SOLUBLE, PbS QDs SURFACE MODIFIED, ARSENIDES, LANTHANIDE NANOMATERIALS, TRANSITION METAL NANOMATERIALS, SPECIALITY CHEMICALS, MAGNETIC NANOPARTICLES, CUSTOM SYENTHESIS, METALIC FOAMS, SCREEN PRINTED BIO SENSOR, LITHIUM ION BATTERY MATERIAL, ITO COATED GLASS, POLYMERS NANO MATERIAL, NANO FABRIC COATINGS, METAL FOILS, PELLETS CHIPS METAL BALLS, WAFERS & TARGETS, SPUTTERING TARGETS, SINGLE CRYSTAL SUBSTRATES, PYROLITIC GRAPHITE, PROTECTIVE EQUIPMENTS, METAL CRUCIBLES, ALUMINA CERAMIC TILES, INORGANIC COMPOUNDS